The purpose of the study reported in this paper was to prepare modified C.I. Pigment Red (PR) 170 to reduce production cost and improve application performance. The structure of the modified pigment was characterised. The colour strength, thermal stability, mobility, aqueous dispersability and ultraviolet (UV) resistance of modified pigments were studied.

Silica fume was added into the diazonium salt solution under acidic condition, followed by the activation to generate new surface. Subsequently, coupling component was dropwise added to the system to form the modified pigments evenly on the surface of silica fume in situ. The structure and properties of the modified pigment were studied by fourier transform infrared spectoscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermal gravity analysis (TG-DTA), UV-visible diffuse reflectance spectra (UV-Vis DRS), and commission internationale de L‘Eclairage (CIE L*a*b*) colour measurements.

The morphology and particle size of the modified pigment were controlled by the modification of the silica fume, and the organic pigment and silica fume formed a core–shell structure. The properties of the modified pigment including colour strength, thermal stability, mobility, aqueous dispensability and UV resistance were improved significantly.

The effect of the amount of silica fume on the thickness of the organic pigment layer and the effect of the thickness of the organic pigment layer on the properties of the modified pigment need to be studied further.

This paper shows a feasible method of the modification of the PR170 with the silica fume, and the modification can improve the properties of the PR170. The use of silica fume to modify organic pigment can realise the reuse of solid waste and reduce the production cost of the organic pigment.

This modification method of the organic pigment is adaptive and it can be adjusted to the modification of other species of the organic pigment.

The modification of the PR170 with the silica fume was carried out in its preparation process, which synchronised the preparation and modification of the organic pigment. The properties of the modified pigment were improved, which were beneficial for their application in inks and coatings.

The purpose of the work reported in this paper is to prepare hybrid pigments fabricated by depositing pigment yellow 12 (PY12) on the surface of silica gel to improve the application performance of the resulting pigments. The particle size distribution, optical properties, thermal stability, water dispersibility and flowability of the pigments with and without silica gel modification were studied.

The hybrid pigments were synthesised with different amount of silica gel. The modified pigments were characterised by Fourier transforms infrared spectroscopy, X-ray diffraction, thermal analysis, scanning electron microscopy and transmission electron microscopy.

The particle size distribution of the modified pigments was found to have been altered significantly. This can be explained by the interaction between pigments and silica gel, which prevented self-aggregation of pigment particles and hence improved the properties of pigments.

Only silica supports and pigment yellow 12 were evaluated. Other pigments could also be studied.

Modification of pigment particles with smaller particle size can increase the efficiency of the modified pigment, in terms of colour shade and tinting strength, due to better particle size distribution.

The paper demonstrates that inorganic core can prevent self-aggregation of pigment particles, and the application properties of such pigment depend on the resulting degree of dispersion of pigment particles.

This study aims to fabricate a cool phthalocyanine green/TiO₂ composite pigment (PGT) with high near-infrared (NIR) reflectance, good color performance and good heat-shielding performance under sunlight and infrared irradiation.

With the help of anionic and cationic polyelectrolytes, the PGT composite pigment was prepared using a layer-by-layer assembly method under wet ball milling. Based on the light reflectance properties and color performance tested by ultraviolet-visible-NIR spectrophotometer and colorimeter, the preparation conditions were optimized and the properties of PGT pigment with different assembly layers (PGT-1, PGT-3, PGT-5 and PGT-7) were compared. In addition, their heat-shielding performance was evaluated and compared by temperature rise value for their coating under sunlight and infrared irradiation.

The PGT pigment had a core/shell structure, and the PG thickness increased with the self-assembly layers, which made the PGT-3 and PGT-7 pigment show higher color purity and saturation than PGT-1 pigment. In addition, the PGT-3 and PGT-7 pigment showed 11%–16% lower light reflectance in the visible region. However, their light reflectance in the NIR region was similar. Under infrared irradiation the PGT-5 and PGT-7 pigment coating showed 1.1°C–3.4°C and 1.3°C–4.7°C lower temperature rise value than PGT-1 pigment coating and physical mixture pigment coating, respectively. And under sunlight the PGT-3 pigment coating showed 1.5–2.6°C lower temperature rise value than the physical mixture pigment coating.

The layer-by-layer assembling makes the core/shell PGT composite pigment possess low visible light reflectance, high NIR reflectance and good heat-shielding performance.