Search results

The purpose of this study is to evaluate the effectiveness of nanocontainer solutions in removing deteriorated and aged polymers commonly used in coating and consolidating archaeological glass.

This study focused on characterizing glass surfaces coated with two commonly used polymeric materials in archaeological glass preservation. Furthermore, the study evaluates the elimination of these coatings from the surfaces by using innovative aqueous systems composed of micellar solutions (MS) and oil-in-water (O/W) Texapon-P microemulsions (TEX). Glass samples coated with selected polymers were subjected to thermal and photochemical aging to simulate natural degradation conditions. This study aimed to evaluate the effectiveness of nanocontainer aqueous systems compared to acetone (Ac), a conventional solvent commonly used for removal procedures. The characterization procedures involved transmission electron microscopy, USB digital microscopy, scanning electron microscopy, color alteration and gravimetric measurement.

The findings indicate that the effectiveness of novel techniques using aqueous nanocontainer systems is quite promising when considering a “green approach” to preserving cultural heritage. Microscopic examination demonstrated the efficacy of MS in effectively removing acrylic and vinyl polymers from the glass surface. Furthermore, TEX proved effective in removing polyvinyl acetate (PVA) over Paraloid B72 (B-72). In addition, the measurement of color alteration values revealed a decrease after using MS compared to the standard sample before applying the polymers, with values of ΔE = 1.48 and 1.82 for B-72 polymer and PVA, respectively.

This research provides nanocontainer solutions for removing aged polymers from the glass surface. This makes the current study a promising step for treating archaeological glass.

This study aims to assess the efficacy of nano-alumina (nano-Al₂O₃) in improving the performance of epoxy adhesives used to assemble archaeological glass. The conservators face a significant problem in assembling this type of artifact. Therefore, the assembling process is considered one of the important stages that must be taken care of to preserve these artifacts from damage and loss.

To evaluate the stability of adhesives, the samples were subjected to artificial aging under varying environmental conditions. Some investigative techniques and mechanical testing were used in this study to evaluate the selected materials. It includes a transmission electron microscope, X-ray diffraction, visual assessment, digital microscope, scanning electron microscopy (SEM), color change and tensile strength test.

The visual evaluation and the digital microscope results showed that the epoxy/nano-Al₂O₃ greatly resisted artificial aging. Although slight yellowing was present, it did not significantly affect the general appearance of the samples. On the other hand, the pure epoxy sample showed cracks of different sizes on its surface due to aging, as evidenced by SEM examination. Furthermore, epoxy/nano-Al₂O₃ has a better tensile strength (11.27 MPa) and slight color change (ΔE = 2.06).

The main objective of the experimental study was to identify appropriate adhesive materials that possess key properties such as non-yellowing and improved tensile strength by conducting various tests and evaluations. Ultimately, the goal was to identify materials that could serve as effective adhesives for assembling the archaeological glass.