The purpose of this study is the development of sustainable and low-formaldehyde emission wood adhesive formulations.

Three-step urea formaldehyde (UF) resin has been in situ modified with calcium lignosulfonate (LS) and/or 1,4 butanediol diglycidyl ether (GE). The structural, chemical, thermal and morphological characterizations were carried out on resin samples. These resins have been applied for particleboard pressing, and UF, UF-LS and UF-GE were evaluated as P2 classes according to EN 312.

The results show that the improved LS- or diglycidyl ether-modified UF wood adhesives were successful in their adhesive capacity, and the formaldehyde content of the final product was obtained as low as 8 mg/100 g. This paper highlights that the presented adhesive formulations could be a potential eco-friendly and cost-effective alternative to formaldehyde-based wood adhesives for interior particleboard production.

Combination of LS and GE resulted in weaker mechanical properties and fulfilled P1 class particleboards due to temperature and duration conditions. Therefore, in situ usage of LS or GE in UF resins is highly recommended for particleboard pressing. Formaldehyde content of particleboards was determined with the perforator method according to EN 12460-5 and all of the particleboards exhibited E1 class. LS was more efficient in decreasing formaldehyde content than GE.

This study provides the application of particleboards with low formaldehyde emission.

The developed LS- and diglycidyl ether-modified UF resins made it possible to obtain boards with significantly low formaldehyde content compared with commercial resins.

The developed formaldehyde-based resin formulation made it possible to produce laboratory-scale board prototypes using LS or GE without sacrificing of press factors and panel quality.

In industrial applications, formaldehyde-based wood adhesives have been used extensively because of their low costs and high reactivity. However, their real-world applications are hindered by some main bottlenecks, especially the formaldehyde emission and usage of nonrenewable raw materials. The purpose of this study is the development of sustainable and formaldehyde-free wood adhesive formulation.

In this study, starch and tannin-based wood adhesive were synthesized. Chemical structures and thermal properties of the prepared bio-based resin formulations were elucidated by using Fourier transform infrared and differential scanning calorimetry analysis, respectively. Laboratory scale particleboard production was carried out to determine the performance of the developed resin formulations. Obtained results were evaluated in dry medium (P2) according to European norms EN 312 (2010). Furthermore, the board formaldehyde content was determined by using the perforator method according to the European Norm EN 12460-5.

The results show that the improved starch and tannin-based wood adhesives were successful in their adhesive capacity, and the formaldehyde content of the final product was obtained as low as 0.75 mg/100 g. This paper highlights that the presented adhesive formulations could be a potential eco-friendly and cost-effective alternative to the formaldehyde-based wood adhesives for interior particleboard production.

Starch-based resins in the liquid form needed to be continuously mixed throughout their shelf life to prevent the starch from settling because it was not possible to dissolve the precipitated starch again after a while. For this reason, starch was given to the chips in powder form while preparing the particleboard.

In conclusion, this study shows that the developed bio-based resin formulations have a high potential to be used for producing interior-grade particleboards instead of commercial formaldehyde-based wood adhesives because the obtained results generally satisfied the interior grade particleboard requirements according to European norms EN 312, P2 class (2010). In addition, it was determined that the produced boards had significantly low formaldehyde content. The low formaldehyde content of the final boards was not because of the resin but because of the natural structure of the wood raw material, press parameters and environmental factors.

The developed bio-based resin system made it possible to obtain boards with significantly low formaldehyde content compared to commercial resins.

The developed bio-based resin formulation made it possible to produce laboratory-scale board prototypes at lower press factors and board densities compared to their counterparts.